| 性能 |
ASTM A240和 ASME SA-240 要求的低機械性能 |
||
| 304 | 304L | 304H | |
|
0.2% 抵消 屈服強度, psi MPa |
30,000 205 |
25,000 170 |
30,000 205 |
|
極限抗張強度, psi MPa |
75,000 515 |
70,000 485 |
75,000 515 |
| 延伸百分比(2英寸或51mm) |
40.0 |
40.0 |
40.0 |
|
硬度, 大., 布氏硬度) RB |
201 92 |
201 92 |
201 92 |
| 測試溫度 |
0.2% 屈服強度 |
||
| °F | °C | psi | (MPa) |
| -423 | -253 | 100,000 | 690 |
| -320 | -196 | 70,000 | 485 |
| -100 | -79 | 50,000 | 354 |
| 70 | 21 | 35,000 | 240 |
| 400 | 205 | 23,000 | 160 |
| 800 | 427 | 19,000 | 130 |
| 1200 | 650 | 15,500 | 105 |
| 1500 | 815 | 13,000 | 90 |
| 抗拉強度 | 延伸 | |
| psi | (MPa) | 百分比 |
| 250,000 | 1725 | 25 |
| 230,000 | 1585 | 35 |
| 150,000 | 1035 | 50 |
| 90,000 | 620 | 60 |
| 70,000 | 485 | 50 |
| 66,000 | 455 | 43 |
| 48,000 | 330 | 34 |
| 23,000 | 160 | 46 |
| 溫度 | 夏氏V形沖擊實驗能量吸收 | ||
| °F | °C | 英尺 ? 磅 | 焦耳 |
| 75 | 23 | 150 | 200 |
| -320 | -196 | 85 | 115 |
| -425 | -254 | 85 | 115 |